    • R-PET or PCR PET

    Trading Films offers post-consumer recycled (PCR) PET films made from 60 to 100% PCR PET resin. They are designed with a high content of recycled PET materials that have been sanitized and reconfigured into PET sheet manufacturing grade resin, making them environmentally sensitive and 100% compliant with sustainability requirements.

    The resins used to produce these PET films are manufactured from post-consumer grade recycled PET bottles using state-of-the-art technology and are fully FDA and EU approved for use in food contact and other product applications. They feature the same performance specifications as other PET films, offering high impact strength and extremely effective barrier properties against water, carbon dioxide, oxygen and nitrogen.

    List of Products with PCR content (Post consumption Recycled)

    All references of products that consume in PET can be produced with PCR content

    Sr. Nº. Reference Description
    1 1022-60% PET from 12 to 75 microns untreated for industrial applications. 60% PCR content
    2 1022-90% PET from 12 to 75 microns untreated for industrial applications. 90% PCR content
    3 1022-100% PET from 12 to 75 microns untreated for industrial applications. 100% PCR content
    4 1009-60% PET from 12 to 36 microns chemically treated 1/S. 60% PCR content
    5 1009-90%+ PET from 12 to 36 microns chemically treated 1/S. 90% PCR content
    6 1009-100% PET from 12 to 36 microns chemically treated 1/S. 100% PCR content
    7 1042-60% PET from 12 to 36 microns chemically treated 1/S and corona 1/S. 60% PCR content
    8 1042-90% PET from 12 to 36 microns chemically treated 1/S and corona 1/S. 90% PCR content
    9 1042-100% PET from 12 to 36 microns chemically treated 1/S and corona 1/C. 100% PCR content
    10 1030-60% PET from 12 to 36 microns corona treated 1/S. 60% PCR content
    11 1030-90% PET from 12 to 36 microns corona treated 1/S. 90% PCR content
    12 1030-100% PET from 12 to 36 microns corona treated 1/S. 100% PCR content
    13 1036-30% White Opaque PET from 12 to 50 microns corona treated 1/S. 30% PCR content
    14 1028-70% PET from 12 to 30 microns heat-sealable inside and corona treated outside or vice versa. 70% PCR content
    15 1043-70% PET from 12 to 36 microns Matte corona treated 1/S. 70% PCR content
    16 1055-70% PET from 12 to 36 microns Matte chemically treated 1/S. 70% PCR content
    17 1015-90% PET from 12 to 36 microns metallized and corona treated 1/S -D.O 2.2. 70% PCR content
    18 1044-60% PET from 12 to 36 microns metallized chemically treated 1/S and corona treated 1/S -D.O 2.2. 60% PCR content
    19 1044-90% PET from 12 to 36 microns metallized chemically treated 1/S and corona treated 1/S -D.O 2.2. 90% PCR content
    20 1048-70% PET from 12 to 36 microns metallized and corona treated 1/S low optical density (susceptor) -D.O 0.30 70% PCR content
    21 1073-PCR content High-barrier metallized PET from 12 to 36 microns -D.O 3.0. PCR container to select
    22 1057-60% PET from 12 to 36 microns gold metallized and corona treated 1/S -D.O 2.2. 60% PCR content
    23 1057-90% PET from 12 to 36 microns gold metallized and corona treated 1/S -D.O 2.2. 90% PCR content
    The % of PCR content can be chosen by the client, in this list we have shown just a few examples
    All references of products that consume in PET can be produced with PCR content

    Properties Method Unit Values
    Physical R-PET@100% PET
    Thickness Internal µ 12 12
    Yield Internal M2/Kg 59.5 59.5
    Mechanical
    Tensile strength MD
    Tensile strength TD    		 ASTM D-882 Kg/cm2 1900
    2000    		 2000
    2100
    Elongation at break MD
    Elongation at break TD    		 ASTM D-882 % 100
    90    		 100
    90
    Surface
    Coefficient of friction St
    Coefficient of friction Dy    		 ASTM D-1894 –
    –    		 0.48
    0.42    		 0.48
    0.40
    Superficial tension ASTM D-2578 Dinas/cm 46 54
    Optical -Haze ASTM D-1003 % 3.5 3.5
    Thermal- Shrinkage ASTM D-1204 % MD/TD 2.0/0.0 2.0/0.0

    Properties Method Unit Values
    Physical R-PET@100% PET
    Thickness Internal µ 12 12
    Yield Internal M2/Kg 59.5 59.5
    Mechanical
    Tensile strength MD
    Tensile strength TD    		 ASTM D-882 Kg/cm2 1900
    2000    		 2000
    2100
    Elongation at break MD
    Elongation at break TD    		 ASTM D-882 % 100
    90    		 100
    90
    Surface
    Coefficient of friction St
    Coefficient of friction Dy    		 ASTM D-1894 –
    –    		 0.50
    0.45    		 0.54
    0.48
    Superficial tension ASTM D-2578 Dinas/cm 52 52
    Optical -Haze ASTM D-1003 % 3.5 3.5
    Thermal- Shrinkage ASTM D-1204 % MD/TD 2.0/0.0 2.0/0.0

    Properties Method Unit Values
    Physical R-PET@70% PET
    Thickness Interno µ 12 12
    Yield Interno M2/Kg 59.5 59.5
    Mechanical
    Tensile strength MD
    Tensile strength TD    		 ASTM D-882 Kg/cm2 1900
    2000    		 1900
    2000
    Elongation at break MD
    Elongation at break TD    		 ASTM D-882 % 100
    90    		 100
    90
    Surface
    Coefficient of friction St
    Coefficient of friction Dy    		 ASTM D-1894 –
    –    		 0.40
    0.36    		 0.40
    0.36
    Superficial tension ASTM D-2578 Dinas/cm 46 46
    Optical -Haze ASTM D-1003 % 45 45
    Thermal- Shrinkage ASTM D-1204 % MD/TD 2.0/0.0 2.0/0.0

    Properties Method Unit Values
    Physical R-PET@100% PET
    Thickness Internal µ 12 12
    Yield Internal M2/Kg 59.5 59.5
    Mechanical
    Tensile strength MD
    Tensile strength TD    		 ASTM D-882 Kg/cm2 1900
    2000    		 2000
    2100
    Elongation at break MD
    Elongation at break TD    		 ASTM D-882 % 100
    90    		 100
    90
    Surface
    Coefficient of friction St
    Coefficient of friction Dy    		 ASTM D-1894 –
    –    		 0.70
    0.60    		 0.70
    0.60
    Superficial tension ASTM D-2578 Dinas/cm 54 54
    Optical -Haze ASTM D-1003 % 2.2 2.2
    Thermal- Shrinkage ASTM D-1204 % MD/TD 2.0/0.0 2.0/0.0

    Properties Method Unit Values
    Physical R-PET@100% PET
    Thickness Internal µ 12 12
    Yield Internal M2/Kg 59.5 59.5
    Mechanical
    Tensile strength MD
    Tensile strength TD    		 ASTM D-882 Kg/cm2 2000
    2100    		 2000
    2100
    Elongation at break MD
    Elongation at break TD    		 ASTM D-882 % 100
    90    		 100
    90
    Surface and Barrier
    MVTR (38ºC-RH90%)
    OTR (23ºC-RH0%)
    Superficial tension    		 ASTM F-1249
    ASTM D-3985
    ASTM D-2578    		 gm/m2/dia
    cc/m2/dia
    Dinas/cm    		 40.0
    3.50
    56    		 40.0
    3.50
    56
    Optical – O.D. ASTM D-1003 % 0.3 0.3
    Thermal- Shrinkage ASTM D-1204 % MD/TD 2.0/0.0 2.0/0.0